High Alumina Brick - AZS Alumina Firebrick Supplied by CNBM

High Alumina Brick - AZS Alumina Firebrick Supplied by CNBM

Ref Price:

Loading Port:: China main port

Payment Terms:: TT OR LC

Min Order Qty:: 1000 pc

Supply Capability:: 10000000 pc/month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Quick Details

Place of Origin:	Jiangsu, China (Mainland)	Shape:	Brick	Material:	Alumina Cement
SiO2 Content (%):	18	Al2O3 Content (%):	49	MgO Content (%):	3
CaO Content (%):	4	Refractoriness (Degree):	Common (1580°< Refractoriness< 1770°)	CrO Content (%):	0.6
SiC Content (%):	0.8	Model Number:	fq036	Brand Name:	cnbm

Packaging & Delivery

Packaging Details:

Plywood tray

AZS firebrick

1)-The different content of ZrO2 led to three model:

	Item	Index
	Item	33#	35#	40#
Chemical Composition(%)	Al2O3	49	49	49
	ZrO2	32.0-34.5	35.0-37	40.0-42.0
	SiO2≤	15.5	14	13
	Fe2O3≤	0.1	0.1	0.1
	TiO2≤	0.05	0.05	0.05
	Na2O≤	1.5	1.4	1.3
Physical Composition	Apparent Porosity(%)	2	1.5	1.3
	Bulk Density(g/m³)	3.8	3.89	4.12
	Cold Crushing Strength(MPa)	350	350	350
	Refractorlness(°C)	1710	1710	1730
	0.2MPa Softening temp. Under load(°C)	>1700	>1700	>1700
	Exudation temp. of Glass Phase(°C)	>1400	>1420	>1430
	Corrosion Resistance of Glass Melt (mm/24h)	1.3	1.2	1.1
	Thermal Expansion(%)	0.8	0.8	0.8
	Glass Phase(%)	20	19	18
Bulk Density(g/m³)	PT.QX	3.4	3.45	3.55
	ZWS	3.6	3.65	3.9
	WS	3.7	3.78	3.92

AZS alumina firebrick supplied by CNBM

Q: In 2016, a few of the traditional refractory materials will be able to survive: From the year 2015 to the year 16 the end of the year, refractories industry presents two kinds of situations: one is a small business, a single product variety and equipment, to meet the demands of both environmental protection and the downstream market, such enterprises are generally in the Qing state inventory;

Q: Introduction of high alumina brick: High alumina brick is one of refractory materials. The main component of this kind of refractory brick is AL2O3. If the content of Al2O3 is higher than 90%, it is called corundum brick. Because of the different resources, the standards of different countries are not identical. For example, European countries limit the content of Al2O3 to high alumina refractories by 42%. In China, the content of Al2O3 in high alumina brick is usually divided into three parts: I, etc. - Al2O3 content, >75%, II, etc. - Al2O3 content is 60 ~ 75%, and the content of Al2O3 is 48 ~ 60%.

Q: What refractory material does cupola lining use?: Materials defined as physical and chemical properties that allow them to be used in a high temperature environment are called refractory materials. Refractory materials are widely used in metallurgy, chemical, petroleum, machinery manufacturing, silicate, power and other industrial fields, the largest amount of metallurgical industry, accounting for 50% ~ 60% of the total output.

Q: What is the standard classification of high alumina bricks and high alumina bricks?: High alumina brick is one of refractory materials. The main component of this kind of refractory brick is AL2O3. High alumina brick refractory clay brick and brick than refractoriness to high. It belongs to high refractory. High alumina brick Al2O3 more, close to the neutral refractory material, can resist acid slag and alkaline slag erosion, because it contains SiO2, so the ability of alkaline slag resistance than acid resistant slag ability is weaker.According to the number of AL2O3 content is divided into, 55,65, 75,80 and so on several grades.

Q: What is the difference between T3 refractory bricks and high alumina refractory bricks?: High aluminum refractory brick brick is all in one type of material classification, the material is AL2O3 high bauxite content above 55%, refractory brick by material into clay bricks, high aluminum brick brick brick corundum brick

Q: What kinds of minerals are there in the five major categories of ore crystal chemistry?: Sulphide. A total of more than 200~300 kinds, followed by the type of silicate minerals, the weight of 0.25% of the crust. Chang Fu is an important nonferrous metal deposit, which is an important source of copper, lead, zinc, antimony and so on. It is of great economic value. The main features are: metal luster, color, streak is deep, low hardness, good thermal conductivity, than the major. Another feature is that because sulfides are often associated with magma, it is very easy to oxidize under the surface supergene action. Except for pyrite (6 ~ 6.5 hardness), the hardness is very low. Such minerals pyrite, chalcopyrite, galena, FeS2 CuFeS2, PbS, Sb2S3, stibnite sphalerite molybdenite, cinnabar HgS MoS2.

Q: What is spalling resistant high alumina brick?: Using bauxite as main raw materials, the introduction of a small amount of ZrO2 (ZrO2 is due to phase transition, between monoclinic and tetragonal type can improve the thermal stability of the products), adding a certain amount of binder and additives, the particle size distribution control mud, forming and sintering of refractory products produced, called anti stripping high alumina brick.

Q: Are there any differences between insulating bricks and refractory bricks?: Heat preservation brick is to emphasize its heat preservation performance generally, not paying much attention to its refractoriness, but refractory brick is exactly the opposite. Different locations will use different materials, I hope we can choose carefully.

Q: How to distinguish the good or bad of the high aluminum brick?: The general high alumina bricks used in the steel, steelmaking, hot blast furnace, electric furnace, blast furnace, reverberatory furnace, rotary kiln lining of industrial furnace in China, mainly composed of a bauxite; sillimanite minerals (including kyanite, andalusite, sillimanite etc.); synthetic material, such as alumina synthesis of mullite, corundum, etc.. High aluminum brick has good quality, high refractoriness, long life and other characteristics, is the main use of refractory brick kiln products, commonly used units can not distinguish the quality and grade of high aluminum brick right in the procurement time, caused by the high prices to buy low grade products, thereby reducing the furnace life therefore, Zhengzhou's Sindh yuan refractory material factory in here is simple to introduce how to identify the quality when purchasing brick high alumina brick.Color: in the purchase of high alumina brick, first of all to see the color, high quality aluminum brick surface smooth, yellow color white, four sides smooth, no broken angle, no cracksWeight: the weight of a block of bricks to be called, according to the standard weight level, high aluminum brick weight of 4.5 kg. Two grade high alumina brick weighs 4.2 kg, three high aluminum brick weighs 3.9 kg, the same level, the same parameters can reach this standard can be regarded as high-quality high aluminum bricks, the opposite is not up to the weight that the quality is good, if there is a crack, four angle uneven, off angle phenomenon, then substandard products, some of the above points to help to the purchaser

Q: How high can aluminum bricks expand at 80O degrees of heat?: The expansion of high alumina brick is not only related to temperature, but also related to its material composition. The refractory temperature of high alumina brick is above 1770 centigrade. The temperature of 800 DEG C has little influence on the expansion of high alumina brick.