Silica Brick for Glass Furnace Application

Ref Price:

Loading Port:: China Main Port

Payment Terms:: TT OR LC

Min Order Qty:: -

Supply Capability:: -

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Specifications

1.high temp Refractoriness Under Load
2.good stability under high temp
3.low pollution
4.Refractory Silica Brick

Silica Bricks for Glass Furnace

,there are series silica bricks for glass furnace, BG-95, BG-96A, BG-96B. high purity silica for brick mading, with science material proporation and technic of products. different calcined machine, automation, short cycle of production.

Item		BG-94	BG-95	BG-96A	BG-96B
Chemical composition	SiO2	≥94	≥95	≥96	≥96
	Fe2O3	≤1.5	≤1.5	≤0.8	≤0.7
	Al2O3+TiO2+R2O		≤1.0	≤0.5	≤0.7
Refractoriness °C		1710	1710	1710	1710
Apparent Porosity%		≤22	≤21	≤22	≤22
Bulk Density g/cm3		≥1.8	≥1.8	≥1.8	≥1.8
True Density,g/cm3		≤2.38	≤2.38	≤2.34	≤2.34
Cold Crushing Strength Mpa		≥24.5	≥29.4	≥35	≥35
0.2Mpa Refractoriness Under Load T0.6 °C		≥1630	≥1650	≥1680	≥1680
Permanent Linear Change On Reheating(%)1500°CX2h		0~+0.3	0~+0.3	0~+0.3	0~+0.3
20-1000°CThermal Expansich10-6/°C		1.25	1.25	1.25	1.25
Thermal Conductivity (W/MK) 1000°C		1.74	1.74	1.44	1.44

$Glass Furnace Application Refractory Silica Brick$

Q: The specific content is what gb/t2608-2012 brick: Quality assessment procedures, packaging, marking, transport, storage, and quality certificates. Suitable for siliceous refractory bricks.

Q: The introduction of silica brick: Brick refers to the content of more than 93% products SiO2. Brick with SiO2 content of not less than 96% of silica as raw materials, adding mineralizer and binder, through mixing, molding, drying, sintering and other processes in the system. The higher the content of SiO2 in silica raw material, the higher the refractoriness of the product. According to the use of brick varieties, divided into: coke oven silica brick, brick for hot blast stove, electric stove with brick, brick for glass furnaces. According to the transformation is divided into: standard bricks, tiles, bricks and general special brick etc..

Q: Such purpose and scope please give me detailed points thank you because I am learning stage: Acid refractory brick is mainly composed of tridymite and cristobalite and quartz and a small amount of residual glass phase.

Q: What is the main material of silica brickIt's common, the kind we see so often!: Higher high temperature strength. The softening start temperature is 1620~1670 degrees. Long term use at high temperature without deformation. The thermal shock resistance is low (the heat exchange in water is 1~4 times). The natural silica is used as the raw material, and a proper amount of mineralizer is used to promote the transformation of quartz into phosphorus and quartz. Slowly sintered at 1350~1430 DEG C in the reducing atmosphere. When heating up to 1450 degrees, the total volume of 1.5~2.2% expands, and the residual expansion can close the kerf and ensure the airtight and structural strength of the masonry.

Q: How much is the highest melting point of silicon?: Acidic silica brick refractories, softening temperature is as high as 1640 to 1670 DEG C, in the long-term use volume is relatively stable under high temperature. More than 94% silica content.

Q: Glass kiln brick for physical and chemical indicators?: Glass kiln with high quality silica brick products according to the standard JC/T615-1996, the single brick is divided into 3 grades: XBG-96, ZBG-96, DBG-96.

Q: Can not use it two brick: Acidic silica brick refractory material, has good ability in acid slag erosion

Q: Common bond brick?: Lime should contain a lot of active CaO, I decompose CaCO3 and MgCO3 not more than 5%, Al2O3+Fe2O3+SiO2 no more than 5%. When the content of large particles, burned Ca-CO3 and over burned lime, the product produced caves, affecting the quality of products.

Q: The difference between clay refractory bricks and refractory brick in the application.: Clay brick features good thermal shock resistance and low price, but high temperature performance is not well integrated, and the long-term use temperature is not higher than 1300 degrees. It is widely used in low temperature parts of various kilns.

Q: What is the silica refractory products?: High silicon content in high temperature expansion sintering temperature between 1390-1410 in furnace arch