Refractory Bricks High Alumina Firebricks Wholesale

Ref Price:

Loading Port:: Shanghai

Payment Terms:: TT OR LC

Min Order Qty:: 10 m.t

Supply Capability:: 8000 m.t/month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

High Alumina Brick ALP80

High Alumina Brick UAL65 - High Alumina Brick

$High Alumina Refractory Bricks / Fireclay Bricks / Insulation Bricks (LQFB)$

High Alumina Refractory Bricks / Fireclay Bricks / Insulation Bricks (LQFB)

High Alumina Brick Rectangular Cordierite Pizza Oven for Pizza Cooking

$High Alumina Refractory Bricks for Steel Industry$

High Alumina Refractory Bricks for Steel Industry

$High Alumina Refractory Bricks for Industrial Kiln$

High Alumina Refractory Bricks for Industrial Kiln

$High Alumina Brick - Refractory Bricks for Pizza Oven$

High Alumina Brick - Refractory Bricks for Pizza Oven

High Alumina Brick - Fire Resistant Furnace Brick

Refractory Bricks High Alumina Firebricks Wholesale

Firebricks Description
High alumina insulating fire brick is a kind of insulation material adopting organic matter as ignition loss substance in order to increase the porosity of refractory,which has such advantages as high porosity, small volume density,good insulation effect,high mechanical intensity,small thermal conductivity and long service life.For various industrial kilns&furnaces,it is a kind of essential refractory for energy saving and temperature preservation.This series of High Alumina fire resistant brick are made of selected high alumina bauxite, kaolin caly,hollow microsphere as the mian material.By shaping at high pressure and sintering at high temperature.

Firebricks Application
High alumina bricks are commonly used in blast furnace,hot blast furnace,the roof of electric furnace,teeming ladle,rotary kiln,regenerator etc.

Firebricks Features
.Low thermal conductivity
.Excellent acid and base slaging resistance
.High refractoriness
.Excellent thermal shock resistance
.Excellent mechanical strength

Firebricks Specification&Pictures

ITEM	UAL48	UAL55	UAL65	UAL75	UAL80	UAL85	ALP80
Refractoriness, ℃	1750	1770	1790	1790	1810	1810	1810
Apparent Porosity,%	22	22	23	23	20	20	18
C.C.S, Mpa	39	44	49	53	55	60	100
Refractories Under Load (0.2Mpa),℃	1420	1470	1500	1520	1500	1520	1550
Reheating Linear Change,%	1450℃x2h 0.1~-0.4	1500℃x2h 0.1~-0.4	1500℃x2h 0.1~-0.4	1500℃x2h 0.1~-0.4	1550℃x2h -0.5~+0.5	1550℃x2h -0.5~+0.5	1550℃x2h -0.5~+0.5
Al₂O₃ Content , %	48	55	65	75	80	85

$Refractory Bricks High Alumina Firebricks Wholesale$

FAQ

Q1 What’s the transport method?

A1 FCL delivery goods with wooden pallet or wooden case by sea; If LCL delivery, must with wooden case; Sometimes need open top, flat rack or bulk cargo.

Q2 What’s the required payment term?

A2 Generally 30% TT as the prepayment, 70% TT before delivery. If need, 100% Irrevocable Letter of Credit or negotiation.

Q3 Which country are our products exported to?

A3 Apart from entire Chinese market, the US, Russia, Japan, Korea, Australia and some Southeast Asian Nations.

Q: What are the requirements for Rubble backfill height?: Backfill should be filled with large stones, big face, small face upward, the decoration is stable, and then use small stones leveling, the gap between the stones can be swept into the slag, gravel, so that the gap filled.

Q: Application characteristics of high alumina brick: Refractoriness. High alumina brick products are advanced varieties of aluminium silicate refractory products, and their refractoriness increases with the increase of Al2O3 content, generally not less than 1750 - 1790 DEG C. If the content of Al2O3 is more than 95% of corundum brick, the refractoriness can be as high as 1900-2000 degrees.

Q: What is the standard size of high alumina brick?: Standard brick: 230 x 115 x 65; four points: 230 x 115 x 40; three points: 230 x 115 x 30; 150 x 120: Brick gable. Light weight brick 1 to 1.7 kilograms; heavy clay superscript brick weighs 3.75 kilograms; light 30 plates 0.79 kilograms; light 40 plates, 1.05 kilograms.

Q: What is the standard classification of high alumina bricks and high alumina bricks?: High alumina brick is one of refractory materials. The main component of this kind of refractory brick is AL2O3. High alumina brick refractory clay brick and brick than refractoriness to high. It belongs to high refractory. High alumina brick Al2O3 more, close to the neutral refractory material, can resist acid slag and alkaline slag erosion, because it contains SiO2, so the ability of alkaline slag resistance than acid resistant slag ability is weaker.According to the number of AL2O3 content is divided into, 55,65, 75,80 and so on several grades.

Q: What is the price of the first grade high alumina brick?: Many factories in Xinmi have high alumina bricks, but they must choose a regular factory. Kuwait refractory level high aluminum brick price at around 1600, the quality of double stable supply

Q: Corundum, high alumina and fireclay refractory difference is what: In fact, they are not consistent with raw materials, corundum refractories can use white corundum, white corundum, brown corundum corundum material, alumina content of these materials is higher than 90%, while the high aluminum refractory material is bauxite, alumina in 90 to less than 70, and clay raw materials the aluminum content is less than 70..

Q: What is the difference between high alumina brick and clay brick?: Lightweight high alumina bricks are usually made of high alumina bauxite clinker with a small amount of clay. After grinding, the bricks are poured and shaped in the form of slurry by gas or foam method. They are fired at 1300~1500 DEG C. Sometimes industrial alumina can be used instead of some bauxite clinker. Used for lining and insulation of masonry kilns, as well as for areas where there is no strong, high temperature molten material erosion and erosion. When contacting the flame directly, the surface contact temperature shall not be higher than 1350 degrees centigrade.

Q: How to reduce the harm caused by two times mullite in high alumina refractory material: Prolong the sintering time and adjust the aluminum content of the high alumina brick.

Q: What causes breakage of refractory bricks?: There are many factors that lead to the damage of refractory brick, can be divided into: the chemical loss (e.g. salt penetration, redox phenomenon), heat loss (burning, thermal shock), mechanical loss (kiln deformation, thrust, brick masonry quality etc.).

Q: What are the lining structures of lime rotary kilns and what are the requirements for refractories?: The current configuration of domestic calcining active lime rotary kiln refractories are as follows: the discharge end of low cement high alumina castable with 3% steel fiber; the cooling zone and the firing zone: dry magnesia spinel brick with high aluminum brick with high temperature; preheating: high alumina brick; low temperature preheating zone: clay brick light clay brick; feeding end: low cement high alumina castable with 3% steel fiber; in addition, brick size also have the corresponding requirements; dimensional tolerances: dimensional tolerances used in different parts of the requirements are not the same, the general control in 2mm; corner damage: general permit edge damage 40mm and 5mm deep within angle loss in the hot and cold surface is allowed to have only one, three edges and the length of not more than 50mm; there are cracks parallel to the use of surface crack is not allowed, cracks of brick surface are allowed.