NUT COKE of Low Phosphorus

Ref Price:

Loading Port:: Tianjin

Payment Terms:: TT OR LC

Min Order Qty:: 100 m.t.

Supply Capability:: 3000 m.t./month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

Foundry Coke Ash 10.5%

Foundry Coke Ash 10%

Calcined Anthracite Made from Taixi Anthracite Coal with stable quality F.C. 93%

Foundry Coke Size 80-120mm

Nut coke of 20-40mm

The Metallurgical Coke of Size is 30 – 90 mm

Metallurgical Coke of Coke Strength after Reactivity 64

CNBM nut coke with normal phosphorous

1. Structure of NUT COKE of Low Phosphorus Description：

Coke is made by high temperature metallurgical coke for blast furnace smelting, casting and gasification. Occurring in the process of coking after recovery and purification of coke oven gas is a high calorific value of fuel, is an important industrial raw material in organic synthesis.

Coke is mainly used for blast furnace ironmaking and used for copper, lead, zinc, titanium, antimony, mercury and other non-ferrous metal smelting of blast furnace, reducing agent, compound and the function of stock column frame.

Blast furnace with Coke instead of charcoal, which laid a foundation for the large-scale of modern blast furnace, is a major milestone in the history of metallurgy.

2. Main Features of the NUT COKE of Low Phosphorus ：

• Quality assurance

• Mutual benefit

• Preferential price

3. NUT COKE of Low Phosphorus Images:

NUT COKE of Low Phosphorus

4. NUT COKE of Low Phosphorus Specification:

Parameters	Guarantee
Moisture (ARB)	5% max
Ash (DB)	12.50% max
Volatile Matter (DB)	1.4% max
Sulphur (DB)	0.7% max
Phosphorus (DB)	0.035% max
CSR	60% min
CRI	28% max
M40	82% min
M10	8% max
Size 30-90 mm	90% min
+90 mm	5% max
-30mm	5% max
Mean Size	52 mm

5. FAQ

We have organized several common questions for our clients，may help you sincerely：

1) How to guarantee the quality of the products？

We have established the international advanced quality management system，every link from raw material to final product we have strict quality test；We resolutely put an end to unqualified products flowing into the market. At the same time, we will provide necessary follow-up service assurance.

2) What are coke's main physical properties?

The average heat capacity is 0.808 kj/(KGK) (100 ℃), 1.465 kj/(KGK) (1000 ℃)

Thermal conductivity is 2.64 kj/(MHK) (room temperature), 6.91 kj/(MHK) (900 ℃);

Ignition temperature (air) is 450-650 ℃.

3) How about your company？

Our company began to export coke when China cancelled 40% of coke export tariffs and quotas on January 1, 2013. We export many kinds of coke, such as CSR60 % and CSR 62% metallurgical coke (met coke), the NUT coke of 20 to 50 mm, coke breeze of 3 to 6 mm, and so on.

Q:What is coke? What is the use?: In addition to coke for iron and non-ferrous metal smelting (metallurgical coke), but also for casting, chemical, calcium carbide and iron alloy, its quality requirements vary. Such as foundry coke, generally require large size, low porosity, high fixed carbon and low sulfur; chemical gasification, strict requirements for strength. But requires good response, high ash melting point; calcium carbide and coke production requirements to improve the fixed carbon content.

Q:Coke and coal is one thing: Coke is bituminous coal under the condition of isolated air, heated to 950-1050 DEG C, after drying, pyrolysis, melting, bonding, solidification, shrinkage and other stages of the final coke, this process is called high temperature coking (high temperature carbonization).Coke is a deep processing of coal products.

Q:Which heroes know, please give the source of the data.: You have to know what kind of coal isBituminous coal and anthracite are determined according to the content of volatile matter in coal,Bituminous coal has C content, geological time is long, but not easy to burn!It is also different from the different producing areas of bituminous coal. Mainly depends on what you want to be low calorific value (not including the vaporization of water vapor latent heat release). High calorific valueTo determine the coal species, industrial analysis, to determine the content of water, ash, volatile, fixed carbon content!That is, there is no formula, mainly the test.Low calorific value = high calorific value -206*H-23MH-- hydrogen contentM-- moisture content (both received base)

Q:What is the density of coke?: Do you want to transport by rail? Ha ha, you might as well ask the freight forwarding clerk, he / she will tell you the various models of the volume and the weight can be installed, the conversion of the density of the pile is more accurate.

Q:Coke is divided into several kinds of specifications ah: (Lord Jiao Meilian) {for precision casting and ductile casting for} fixed carbon above 86; sulfur ash is below 0.5; 12; 1.5: volatile fiddle coke grain size 4cm--8cm or above 10cm: fixed carbon furnace for {}} setting common casting coke particle size 25cm:{for precision casting and ductile casting for 3 more than 88 tons of sulfur ash; 0.5; 10; 1.5: volatile foundry coke particle size 25cm:{type applicable to the above all high precision ductile casting export and international index: {8cm} fiddle coke for common casting and casting products such as strict fire pump fittings; fasteners such as high fixed carbon above 788385} sulfur: {for copper, aluminum, plastic, chemical coke} fixed carbon above 83 gas coal coke: {for carbon monoxide gas extraction, rich gas} fixed carbon about 78 coal coke: {casting parts annealing, Coke, coke, civilian chemical copper, aluminum, plastic} fixed carbon about 65 coke, coke coal: {civil casting parts of annealing, chemical coke}

Q:What are the ingredients of coke: Metallurgical coke is coke, coke, iron alloy coke and non-ferrous metal smelting coke ". Since more than 90% of metallurgical coke is used for blast furnace ironmaking, it is often referred to as coke.Coke is a special and molten iron cupola coke. Coke is the main fuel cupola molten iron. Its role is to melt the burden and make the hot metal overheating, the support column to maintain good ventilation. Therefore, the foundry coke should have large blocks, low reactivity, porosity is small, with impact crushing strength, low ash and sulfur enough.

Q:How to determine the maturity of coke or not?: The degree of fragmentation of coke: refers to the different levels of coke accounted for the percentage of total coke production. The particle size of coke is very important in blast furnace smelting. The coke block is uniform, the gap is large, the resistance is small, and the furnace condition runs well.Breaking strength of metallurgical coke (M40 drum index)The breaking strength of metallurgical coke is an index to reflect the breaking resistance of coke.Wear resistance of metallurgical coke (M10 drum index)The wear resistance of metallurgical coke is an index to reflect the wear resistance of coke.

Q:What are the quality indicators of coke: Different uses of different coke porosity index requirements, the general requirements of metallurgical coke porosity in the 40 ~ 45%, 35 ~ 40% in coke, coke export demand in about 30%. Coke crack degree and the porosity level, and the coking coal has a direct relationship, such as coal based coke refining, crack, high porosity, low strength; with coal as the foundation of the coal refining coke crack less, low porosity and high strength. The strength of coke is usually represented by two indices of crushing strength and abrasion resistance. Coke crushing strength refers to coke can resist foreign impact force without ability along cracks or defects at the broken, represented by the M40 value; wear strength of coke coke refers to the ability to resist external friction without surface of glass forming debris or powder, said M10. The cracking degree of coke affects the M40 value of its breaking strength, and the pore structure of coke affects the M10 value. There are many methods for determination of M40 and M10 value method, commonly used in our country the German migon drum test. Evaluation of the quality of coke, 1 of sulfur in coke: sulfur is a harmful impurity of iron smelting, which reduce the quality of pig iron. The sulfur content in the pig iron is more than 0.07%. 11% of the sulfur from the blast furnace charge into the furnace comes from the ore, and the other comes from the limestone; the other is from the coke, so the coke is the main source of sulfur in the charge of the 82.5% of the charge. Sulfur content in coke directly affects the production of blast furnace. When the sulfur content in coke is greater than 1.6%, sulfur increased 0.1%, the amount of coke increased 1.8%, limestone amount increased 3.7%, 0.3% increase in amount of ore blast furnace output to reduce the sulfur content under 1.5 - 2.0%. metallurgical coke is not greater than 1%, the use of large and medium-sized metallurgical coke content in blast furnace is less than 0.4 - 0.7%

Q:Coke is how to participate in the steel, and the pellets, sintering, a piece of the furnace in the furnace or in other containers: Molten iron is produced in a reducing atmosphere of the blast furnace, which is then supplied to the steelmaking plant for steelmaking.

Q:Coke is how to produce, what is its purpose?: Under the condition of air isolation, the bituminous coal is heated to 950-1050 DEG C, which is finally made into coke by drying, pyrolysis, melting, bonding, solidification and shrinkage. Coke oven gas produced in the process of coking and recovery is not only a high calorific value of fuel, but also an important industrial raw material for organic synthesis.

1. Manufacturer Overview
Location
Year Established
Annual Output Value
Main Markets
Company Certifications

2. Manufacturer Certificates
a) Certification Name
Range
Reference
Validity Period

3. Manufacturer Capability
a)Trade Capacity
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range