FC Magnesite carbon bricks for the end of EAF tap hole
Specification :
Grade | MgO (%) | C (%) | AP (%) | B D (g/cm3) | CCS (MPa) | Hot temperature Bending strength (MPa) ≥1400°C30mm |
RGMT -14A | ≥78 | ≥ 14 | ≤4 | ≥2.95 | ≥40 | ≥12 |
Product application: Used for the tap hole of eaf .
Production Technics:
1. Based on fine quality fused magnesia and high purified flake graphite ,
Product features:
1. High refractoriness :1850°c:
2. ,excellent anti-oxidation,
3. high strength :40 Mpa ,
4. perfect thermal Stability;
5. instructure density , low apparent ( less than 4%)
6. Resist the erosion and spall,
7.high abrasion- resistance strength ,
8. perfect ability Of anti-slag;
9. Difficult hydration,
10.can be used for long time.
FAQ
Q1: How do you control the products quality?
A1: With strict quality control system throughout the materials selection and production process, our refractory and ceramic fiber products quality is effectively controlled to meet customer requirements.
From the raw materials selecting, our quality control begin. The quality certificates of raw materials are required and each batch will be tested before using. During production, the quality control are conducted by workers and then each piece will be sorted and examined by quality supervis
Q2: What`s the lead time for my order?
A2: It depends on customers’ requirements and our production schedule. And usually we need 30-60 days for refractory bricks,10-25 days for unshaped refractory materials and 10-20 days for ceramic fiber blankets.
Q3: Can you offer Door-to-Door delivery?
A3: Yes, but only for some countries such us U.S., UAE, Saudi Arabia, Iran, and Russia, etc.
- Q: What is the ratio of magnesia refractory bricks to brine? For example, what is the difference between the 97 and 95 with 92 brick brick brick material mixed with brine ratio?
- In addition to the brine binder burned magnesia brick and sulfite pulp waste liquid, Magnesium Sulfate solution binder is generally around 3%
- Q: The index of magnesia brick
- Room temperature compressive strength≥（MPa）（15－25－）24.5－24.5－24.5－24.5－40－40－40
- Q: High purity magnesia brick masonry mortar for what?
- High purity aluminum is 99.99, the first is not pollution, the stove is high magnesia brick masonry, 95% and 97% purity magnesia brick is for a long time did not find a good bit of fireclay, do not know what to build, now used light burned US powder and heavy burned magnesium plus brine built, with 2 months a griddle doesn't stick on magnesium brick, a touch off, there is no good sintering
- Q: Manufacture of various refractory magnesia brick mainly comes from Magnesium Oxide, what kind of ore?
- Manufacture of various refractory magnesia brick Magnesium Oxide, mainly from magnesite.
- Q: Refractory brick, high alumina brick, magnesia chrome brick, magnesia brick, clay brick, which type of high temperature refractory brick?
- High alumina brick clay brick up to 1700 degrees above 1500 degrees -1750 degrees of magnesia brick and magnesia chrome brick 1500-1650 degrees, I is the production of clay brick, brick my temperature at 1500-1700 degrees. Specific depends on what kiln, brick is only part of it
- Q: Magnesia brick
- Magnesia brick have high refractoriness, alkali slag good performance, high load softening temperature, but poor thermal shock resistance. The sintering magnesia brick brick magnesite as raw material, crushing, proportioning, mixing, forming, in 1550 ~ 1600 degrees firing, high purity products firing temperature is over 1750 DEG C. Don't add chemical bond magnesia brick is appropriate in magnesia, through mixing, molding and drying
- Q: How to identify the fused magnesia brick and sintered magnesia brick
- Magnesia brick (magnesite brick) basic refractories Magnesium Oxide content of more than 90%, with the main crystalline phase of periclase
- Q: Process for producing magnesia chrome brick
- The fine powder compacts after calcination produced by magnesia - chrome ore grinding method, brick with magnesia coarse particles, are effective measures to eliminate the effect of loose. Compared with the common magnesia chrome brick, the magnesia chrome brick made by this method has lower porosity, higher compressive strength, higher softening temperature and higher flexural strength. Compacts with chrome magnesite powder, magnesia chrome brick by synthetic magnesia chrome sand made of high-temperature calcination, slag resistance and high temperature strength are better than other magnesite chrome brick.
- Q: How do you differentiate between the two clearly? Where is the key? Thank you
- Magnesia brick (magnesite brick) basic refractories Magnesium Oxide content of more than 90%, with the main crystalline phase of periclaseGeneral can be divided into sintered magnesia brick (also called burnt magnesia brick) and chemically bonded magnesia brick (also known as the two major categories of not burned magnesia brick). Purity and high firing temperature of magnesia, due to the direct contact of periclase grains, known as direct bonded magnesite brick; made of fused magnesia bricks called electrically fused magnesite brick.
- Q: Magnesite chrome brick, magnesia chrome brick indicators? What is the price?.
- If you want to know the indicators of chrome brick, magnesia chrome brick must know you are in what furnace above, there is in what position
Send your message to us
Magnesite Brick - FC Magnesite Carbon Bricks for EAF Tap Hole
- Ref Price:
-
- Loading Port:
- Tianjin
- Payment Terms:
- TT OR LC
- Min Order Qty:
- 10 m.t.
- Supply Capability:
- 10000000 m.t./month
OKorder Service Pledge
OKorder Financial Service
Similar products
Hot products
Hot Searches
Related keywords