Magnesite Alumina Spinel Brick - Refractory Bricks

Inquire Now

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Packaging Details:	Wood carton box:10pcs/carton wooden pallet:544pcs/pallet
Delivery Detail:	15 Days deposit

Specifications

1. Pure raw material
2. less impurity content
3.through high pressure forming and high temperature burning of brick

1.Pure raw material, less impurity content; through high pressure forming and high temperature burning of brick.

2. The product has advantages of well able to bear erosion, spalling-resistance and high temperature resistant.

3. The product is widely used in transition zone of large dry-process cement rotary kiln.

	LMLJ-80		LMLJ-75
Item\Label and Standard	Standard	Typical Value	Standard	Typical Value
MgO,%	≥80	85.5	≥75	81.2
Al₂O₃, %	8~15	10.2	8~15	9.83
apparent porosity, %	≤17(18)	16	≤18(19)	16
0.2MPa refractoriness under load °C	≥1700	1800	≥1650	1750
cold crushing strength ,MPa	≥40	57	≥40	68
thermal expansion(1100°C,cooling water),times	≥20	20	≥5	16

$Magnesia-Hercynite Brick, Refractory Bricks, Magnesia-Hercynite Refractory Brick$

Q: What are the uses of magnesia spinel brick in the industry?: Used to make ladle casting material, greatly improve the corrosion resistance of steel lining. It is widely used in steel making refractory. The preparation of high-quality pre synthesized spinel provides a new raw material for the production of unshaped and unshaped high purity refractories

Q: What is the primary crystal phase? What is the secondary phase?: There are structure of refractory refractory material in the crystal phase, especially the direct combination of high melting point and so on, the resistance to high temperature also tend to benefit. Compared with the ordinary brick, the second phase of the refractory products, make the products refractoriness under load are improved. Many according to mineral composition of refractory material named, such as mullite corundum brick, corundum mullite brick, is its main crystal phase and the second phase composite named. The former is mainly crystal phase, the latter is sub crystalline phase.

Q: Spinel refractory brick air-cooled razheng times: The ingredients are magnesium, aluminum, oxygen.

Q: Is magnesium spinel harmful to the body? Such as title magnesium spinel, harmful to the body?: Extremely harmful! Studies have shown that brain tissue has affinity for aluminum, and excessive deposition of aluminum in brain tissue can cause memory loss, mental retardation, slow action and aging.

Q: Spinel compound brick composite layer pollution layer does not affect the use of theoretical basis for it: The study of mg Al spinel synthesized with MgO raw materials and Al2O3 raw materials (calcined alumina or alumina) has begun as early as 1930s. Magnesia alumina spinel was synthesized from industrial alumina and activated alumina in 1939 and used for making bricks. In 40s, people found that the addition of alumina powder in magnesia could improve its thermal stability, this is actually a spinel bonded brick. When the magnesia brick is mainly used in cement kiln, but in addition to the production of white cement kiln, it was replaced by magnesia chrome refractories.

Q: What is the high-grade magnesia spinel brick?: Using magnesia as main raw materials, matrix co milling with magnesia and bauxite as alkaline products, high temperature burning, called magnesia brick, also called the first generation of periclase spinel brick.

Q: What is the structure of magnesium aluminate spinel?: Mg Al spinel is a six square dense stack of equiaxed crystals

Q: The difference between aluminium refractory and magnesia refractory: The difference between the two is one is neutral, one is alkaline, the original product is different naturally.

Q: What is the significance of the synthesis of mg Al spinel? What are the main approaches?: Because the thermal expansion coefficient of magnesia alumina spinel is small, the thermal shock resistance of refractory products with its bonding phase is relatively improved.

Q: Characteristics of sintered spinel used in refractory zzjsnc: For the production of castable for ladle lining steel plate greatly improve the anti erosion ability. It is widely used in steelmaking refractories provides new raw material for the production of high quality synthetic stone pre sintered spinel prepared amorphous and amorphous high purity refractory material