Low Porosity Fireclay Brick
- Ref Price:
-
- Loading Port:
- China Main Port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- -
- Supply Capability:
- -
OKorder Service Pledge
OKorder Financial Service
You Might Also Like
China clay brick of Al2O3 content in more than 40% more commonly, Fe2O3 content is less than 2.0 ~ 2.5%.
Ingredients in the clinker is 65 ~ 85%, combined with clay for 35 ~ 15%.To combine pieces of clay and fine
grinding of clinker grinding, again with the clinker particles mixture material dry clay and high pressure molding,
firing under about 1400 ℃, with good performance.Clay bricks under high temperature in weak acid, alkaline
slag erosion resistance is a bit poor, but enhanced with Al2O3 content increase.Thermal stability of the silica brick,
magnesite brick (see magnesia brick), etc.
Clay refractory abundant raw materials, processing is simple, cheap, is more widespread and more so than
any other refractory use: used for blast furnace, hot stove, cupola, ladle and pouring system and soaking pit,
heating furnace, non-ferrous metal melting furnace, silicate and chemical industry with kiln and all thermal
technology equipment of chimney and flue, etc.
1. Manufacturer Overview |
|
|---|---|
| Location | |
| Year Established | |
| Annual Output Value | |
| Main Markets | |
| Company Certifications | |
2. Manufacturer Certificates |
|
|---|---|
| a) Certification Name | |
| Range | |
| Reference | |
| Validity Period | |
3. Manufacturer Capability |
|
|---|---|
| a)Trade Capacity | |
| Nearest Port | |
| Export Percentage | |
| No.of Employees in Trade Department | |
| Language Spoken: | |
| b)Factory Information | |
| Factory Size: | |
| No. of Production Lines | |
| Contract Manufacturing | |
| Product Price Range | |
Send your message to us
Low Porosity Fireclay Brick
- Ref Price:
-
- Loading Port:
- China Main Port
- Payment Terms:
- TT OR LC
- Min Order Qty:
- -
- Supply Capability:
- -
OKorder Service Pledge
OKorder Financial Service
Similar products
Hot products
Hot Searches
Related keywords