High Alumina Fireclay Brick (Al2O3 37%) System 1

High Alumina Fireclay Brick (Al2O3 37%)

Ref Price:

Loading Port:: Qingdao

Payment Terms:: TT OR LC

Min Order Qty:: 17 m.t

Supply Capability:: 10000 m.t/month

Inquire Now

Add to My Favorites

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

You Might Also Like

$Fireclay Brick for Cement Kiln Refractory Use$

Fireclay Brick for Cement Kiln Refractory Use

$Fireclay Brick for Electric Arc Furnace Refractory$

Fireclay Brick for Electric Arc Furnace Refractory

Fireclay Brick - Standard Size/Standard Dimensions

$Fireclay Brick - Fire-resistant Refractory Low Porosity for Glass Furnace Regenerator$

Fireclay Brick - Fire-resistant Refractory Low Porosity for Glass Furnace Regenerator

Furnace Used High Duty and Super Duty Fireclay Brick with Low Porosity

$Anchor Brick, Refractory Brick, Fireclay Brick for Ceramics Tunnel Kiln$

Anchor Brick, Refractory Brick, Fireclay Brick for Ceramics Tunnel Kiln

Fireclay Brick with Al2O3 Content 75-80% Composite

Fireclay Brick - DRL 125 Brick Fired Furnace Brick Lining

General Information
CMAX high alumina firebricks are classified according to alumina content ranging from 48% to 90%.

Feature
Low thermal conductivity
Excellent acid and base slagging resistance
High refractoriness
Excellent thermal shock resistance
Excellent mechanical strength

Application
CMAX high alumina bricks are commonly used in blast furnace, hot blast furnace, the roof of electric furnace, teeming ladle, rotary kiln, regenerator, etc

ITEM	UAL48	UAL55	UAL65	UAL75	UAL80	UAL85	ALP80
Refractoriness, ℃	1750	1770	1790	1790	1810	1810	1810
Apparent Porosity,%	22	22	23	23	20	20	18
C.C.S, Mpa	39	44	49	53	55	60	100
Refractories Under Load (0.2Mpa)，℃	1420	1470	1500	1520	1500	1520	1550
Reheating Linear Change,%	1450℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1500℃x2h 0.1～-0.4	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5	1550℃x2h -0.5～+0.5
Al₂O₃ Content , %	48	55	65	75	80	85	82

Fireclay Brick with Al2O3 Content around 37%

Q: What is the specific heat of a refractory bricks (clay)?: Approximately it's about 2000; M3 specific heat is wrong with this argument, two degree clay is 1730 degrees, three degree clay is 1690 degrees, clay bricks are mixture, bulk density, 1900KG&#47, only elementary substance has specific heat refractoriness.

Q: how much is the content of the high alumina of refractory brick?: linear?change?on?reheating is small and Slag resistance is good, matte smelting, good thermal shock resistance used refractory materials should be resistant to high temperature: In front of the furnace, the temperature can reach 1800, copper blowing. The maximum temperature in the smelting furnace area is on the top, pyro-refining and electrorefining, magnesia chrome brick, magnesia chrome castable, magnesia alumina brick. The commonly used refractory materials is direct-bonded?magnesia-chrome?bricks, which has large volume density. manufacturing technique of copper smelting consists of five parts, Clay brick

Q: Clay brick, red brick, always fried brick how to do?: Clay brick and red brick are of very important quality and must not contain sand or gravel.

Q: What is the meaning of special shaped refractory brick material n-2b?: In fact, there are many kinds of refractory bricks, titanium, high alumina refractory brick, after drying. The mineral composition of the clay brick is mainly kaolinite (Al2O3·2SiO2·2H2O) and 6% ~ 7% impurities (K, etc.). Clay refractory bricks are iron oxide sintered by 50% soft clay and 50% hard clay clinker ingredients according to a certain granularity requirements under the high temperature of 1300 ~ 1400 degrees), perlite

Q: the refractory brick in glass furnace burner was burning, the bricks on both sides of the fire hole were burning the blocked it, what will cause brick burning?: The firebrick in glass melting furnace is mainly consisted of zircon brick, other ordinary refractory materials can not effectively prevent the erosion of glass solution. Because the glass melting liquid is eutectic mixture compared to the refractory bricks, it penetrates into the refractory brick and reduces its original performance, simply speaking, the glass melting liquid dissolves the refractory bricks as eutectic mixture .

Q: What are the properties of clay bricks?: Clay brick is very important. It can make clay brick not only with high refractoriness, but also can be used in many high temperature thermal equipment. The brick brick has better resistance to hot and cold, and the water cooling can reach 10~25 times at 850 centigrade. Clay brick can resist weak acid slag corrosion, the resistance to alkaline slag is slightly worse, increasing the content of Al2O3, can improve the ability of alkali resistance slag.

Q: What is sintered non clay brick?: According to the production process can be divided into sintered brick and non sintered brick, in which non fired brick can be divided into compressed brick, steam brick and autoclaved brick, etc., according to whether or not the hole can be divided into ordinary brick, porous brick, hollow brick.

Q: What is the life of an old fashioned refractory brick kiln transformed into a flat topped tunnel kiln? what material should be used to transform the old fashioned refractory bricks vault kiln to flat tunnel kiln, and how long is the service life?: High alumina brick and hanging brick are ok.

Q: What is the difference between the refractory bricks, hand-made bricks and the machine pressure bricks?: Hand-made brick mainly produces brick that is not easy to produce molding Machine pressure brick adopts 100 tons of press machine to mold the density of hand-made brick is not enough, it's light; machine pressure bricks can only produce bricks that produce molding at a time, hand-made bricks mainly adopts hydraulic vibration molding machine