• High Alumina Casting Steel Refractory Brick System 1
High Alumina Casting Steel Refractory Brick

High Alumina Casting Steel Refractory Brick

Ref Price:
get latest price
Loading Port:
Shanghai
Payment Terms:
TT OR LC
Min Order Qty:
1 m.t.
Supply Capability:
11 m.t./month

Add to My Favorites

Follow us:


OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Specifications

Specifications 
1. AL2O3 : 40%-75%. 
2. Can according to customers' requirements. 
3. Used for Steel industry casting steel.

Specifications

1. AL2O3 : 40%-75%. 
2. Can according to customers' requirements. 
3. Used for Steel industry casting steel.

Casting steel refractory brick,Refractory brick for Casting steel,Casting steel brick

Features and advantages:

1. High refractoriness.

2. Good spalling resistance and wear resistance.

3. Good corrosion resistance.

4. Good thermal shock resistance.

5. High mechanical strength.

6. High-temperature creep rate is low.

7. Good volume stability at high temperature.

 Physical and chemical indicators:

Item

SN-40

KN-40

XN-40

ZN-42

 AL2O3 , %  ≥

40

40

40

40

 Refractoryiness, °C ≥

1710

1710

1710

1710

 Apparent Porosity,%

15-23

≤22

15-25

≤23

Cold Crushing Strength ,Mpa




≥19.6

Refractoriness Under Load,°C

≥1370

≥1370



Permanent Linear Change

(1350°C,2h),%



0~-0.3



Q: What are the high aluminum bricks made of?
The amount of refractory mud accounts for about 6% of the brick weight
Q: What are the reasons for the spalling of refractory bricks in the production of lime kiln?
Therefore, the choice and masonry of refractory bricks are of vital importance. If there is a brick kiln kiln off block process of reproduction, is now because of the use of refractory brick kiln material mostly three grade high alumina bricks. The content of AL2O3 is about 55%, of which the content of Fe2O3 is about 2%, which is weak, and the alkali corrosion resistance is a little worse. In a containing three grade high alumina bricks in the composition of AL2O3, Si2O3, and other elements also contain K, Na trace, were the most, thus causing the system of the low melting point is very low, even at 1400 DEG C has been liquid phase, and generate CaAL12O19 limestone and calcium feldspar etc.. Form corrosion loss. Therefore, a long time will cause the loss of block. On the one hand, it may be caused by construction.
Q: Density of high alumina bricks
The density of high alumina bricks is determined according to the price. The average density is between 2.3-2.5g/cm3. The higher the density, the higher the price, the higher the aluminum bricks are in the industry. More than 2.4 are required.
Q: What materials are used for roof insulation?
The other one is inorganic insulation materials, such as Portland, rare earth insulation, the thickness should be 5 cm or more, up to the high cost of auxiliary materials of construction, to reinforce, new inorganic insulation material, the material thickness, on the line of 2-3 cm, direct smear on the top of the house, without auxiliary material, than the price of wool, high aluminum silicate cotton.
Q: Aluminum content 38, silicon content 55 What refractory bricks?
Semisilica brick: the content of Al2O3 is 15% ~ 30% of aluminium silicate refractory products. Manufacturing products are semi silica quartz containing impurities or native clay kaolin, refractory clay or kaolin beneficiation tailings and the pyrophyllite
Q: Can high alumina brick resist carburizing?
The key is to look at the content of Fe3O2 metal oxides (so-called anti carburizing brick generally refers to the content of Fe3O2 less than 1% clay brick and Gao Lvzhuan) just a photo shoot, out for everyone to see, high alumina brick common in reductive atmosphere has been chalking up.
Q: What are the requirements for refractory materials in heat treatment furnace?
The structural strength of high temperature is evaluated by loading softening point. Load softening point is that under certain pressure (2 kg/ cm 2 = 0.2MPa) under the condition of heating rate to heating, measured the sample deformation (deformation for the original sample 0.6%) temperature. This temperature is called the softening point of the refractory. Sample size is Phi 36 x 50mm.
Q: Is glass wool inorganic thermal insulation material?
Yes, glass wool belongs to one kind of glass fiber. It is a kind of man-made inorganic fiber. Therefore, in the field of thermal insulation materials classified as inorganic insulation materials.
Q: What is the difference between metal compounds and metal solid solutions?
A series of intermetallic compounds occurring between transition metals in intermetallic compounds. The most important are L sigma sigma phase and ves phase, they are topologically close packed (TcP) phase, they consist of a small atomic radius of a dense layer, which is inlaid with a large atomic radius of atomic structure, this is a highly dense pile. In addition to atomic size factors, their formation is also influenced by the concentration of electrons.
Q: What should be used as binder for making high alumina bricks?
Bond for making high alumina brick: soft clay has good plasticity, so the high alumina brick is usually made of soft clay as bond. However, the free Al2O3 free SiO2 and bauxite clinker clay in under 1200 degrees occurred two times of Mullization reaction, generate large volume expansion, silicon porosity, strength reduction. Therefore, the amount of clay powder in the ingredient should be no more than 5%.