High Alumina Brick - High Temperature Fireproof Refractory High Alumina Bauxite Grog Brick for Kiln Furnace/Coke

High Alumina Brick - High Temperature Fireproof Refractory High Alumina Bauxite Grog Brick for Kiln Furnace/Coke

Ref Price:
get latest price
Loading Port:
China main port
Payment Terms:
TT OR LC
Min Order Qty:
2000 pc
Supply Capability:
8000000 pc/month

Add to My Favorites

Follow us:


OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Product Description

Packaging & Delivery

Packaging Details:1.On wooden pallets with plastic cover:Wooden pallet size:930*930mm load weight of each pallet:1.5-2.0 tons 2.According to customer's demands
Delivery Detail:within 30 days



What is the details of our grog brick?

1.Made by bauxite clinker and binder through Crushing,Mixing,Shaping,Drying and high temperature Sintering.

2.Al2O3 content is 48%-80%.

3.Main mineral components are corundum and mullite phases.

4.Refractoriness is usually above 1770°C,refractoriness under load is 1420-1550°C.It is a neutral refractory material so that it enjoys excellent resistance to acid and alkali corrosion.

5.Working temperature:1350°C -1650°C.

What is the Technique Data of our grog brick?

Item

Index

International code name

SK35

SK36

SK37

SK38

SK40

Al2O3 %

48

55

65

75

80

Fe2O3 %

2

2

2

2

2

Refractoriness °C

≥1750

≥1770

≥1790

≥1790

≥1790

Apparent porosity %

≤22

≤22

≤23

≤23

≤21

Cold crushing strength Mpa

39

44

49

54

65

Refractoriness under load(0.2MPa) °C

≥1420

≥1470

≥1500

≥1520

≥1530

Reheating Linear Change (1500°C 2h) %

+0.1~ -0.4

*1450°C

+0.1~ -0.4

+0.1~ -0.4

+0.1~ -0.4

+0.1~ -0.

High Temperature Fireproof Refractory High Alumina Bauxite Grog Brick for kiln furnace/coke


Q: What is the heat preservation material used in a laboratory furnace?
Asbestos, high alumina brick, or carbonized silicon are often used.Thermal insulation materials are generally used to guide heat coefficient less than or equal to 0.2 of the material. Thermal insulation material development is very fast, and in industry and building the use of good insulation technology and materials, often can get twice the result with half the effort. Each ton of mineral cotton insulation used in the building saves one ton of oil a year.
Q: What's the difference between high alumina refractory bricks and high alumina refractory bricks?
The chemical pH value of high alumina refractory brick belongs to neutral and alkaline refractory brick, and clay refractory brick belongs to neutral and acid refractory brick.
Q: How are the high alumina bricks fired?
Generally, the high alumina bauxite is added with a small amount of clay. After being ground, the gas is injected and shaped in the form of slurry by the way of gas attack or foam, and it is burnt at 1300~1500 DEG C. Sometimes industrial alumina can be used to replace part of bauxite clinker. Used for lining and thermal insulation of masonry kilns, as well as for areas where there is no high temperature, high melting material erosion and erosion effects. When touching the flame directly, the touch temperature shall not be higher than 1350 degrees.
Q: What is the difference between T3 refractory bricks and high alumina refractory bricks?
High aluminum refractory brick brick is all in one type of material classification, the material is AL2O3 high bauxite content above 55%, refractory brick by material into clay bricks, high aluminum brick brick brick corundum brick
Q: What materials are used for roof insulation?
There are two kinds: one is a kind of cotton insulation board, such as rock wool board, aluminum silicate cotton board, but this is not environmental protection, harmful to life, foam board (this fire safety factor minimum), these relatively cheap.
Q: Can high alumina brick resist carburizing?
The key is to look at the content of Fe3O2 metal oxides (so-called anti carburizing brick generally refers to the content of Fe3O2 less than 1% clay brick and Gao Lvzhuan) just a photo shoot, out for everyone to see, high alumina brick common in reductive atmosphere has been chalking up.
Q: The difference between ordinary and diatomite brick refractory brick
Refractory brick belongs to a large class, according to different materials used are divided into: high alumina brick, dolomite brick, magnesia chrome brick, magnesia spinel brick, phosphate brick, carborundum brick, brick, mullite bricks etc..
Q: What does refractory consist of?
According to the chemical characteristics of refractory raw materials can be divided into acidic refractory materials, such as silica, zircon etc.; neutral refractory raw material, such as corundum, bauxite, mullite (acidic) (acidic), Ge (alkaline) iron and graphite; alkaline refractory materials, such as magnesite, dolomite, magnesium sand calcium sand.
Q: How high can aluminum bricks expand at 80O degrees of heat?
When an object is heated, the particle moves faster and thus occupies additional space. This phenomenon is called dilation.
Q: What are the categories of bricks?
Ordinary brick size of 240 mm * 115 mm * 53 mm, according to compressive strength (Newton / square millimeter, N / mm2) size is divided into MU30, MU25, MU20, MU15, MU10, MU7.5, these intensity levels.