Sodium Naphthalene Sulfonate Formaldehyde Made in China

Sodium Naphthalene Sulfonate Formaldehyde Made in China

Ref Price:
get latest price
Loading Port:
Qingdao
Payment Terms:
TT OR LC
Min Order Qty:
1000 kg
Supply Capability:
500000 kg/month

Add to My Favorites

Follow us:


OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing


        Sodium Naphthalene Sulfonate Formaldehyde Made in China


Sodium Naphthalene Sulfonate Formaldehyde Made in China       


Naphthalene Sulfonate Formaldehyde Product Description 
High Range Water-Reducing Admixture 
Sodium Naphthalene Sulphonate Formaldehyde, Poly Naphthalene Sulfonate Formaldehyde Condensate,Concrete Admixture

 

Naphthalene Sulfonate Formaldehyde Uses 
Sodium Naphthalene Sulphonate Formaldehyde produces concrete with extremely workable characteristics referred to as high slump. PNS also allows concrete to be produced with very low water/cement ratios at low or normal slumps. 
Sodium Naphthalene Sulphonate Formaldehyde is ideal for use in prestress, precast, bridge deck or any concrete where it is desired to keep the water/cement ratio to a minimum and still achieve the degree of workability necessary to provide easy placement and consolidation

 Sodium Naphthalene Sulfonate Formaldehyde Made in China

Sodium Naphthalene Sulphonate Formaldehyde Specification: 

Items

Specifications

Type

FN1

FN2

FN3

Visual appearance

Dark Brown Power

Light Brown Powder

Light Brown Powder

Fineness(0.315mm remains),%

≤15

≤15

≤15

Solid content, %

≥92

≥92

≥92

pH value(20℃)(5% solution)

7-9

7-9

7-9

Sodium sulfate content,%

≤5.0

≤10

≤18

Chloride content,%

≤0.3

≤0.4

≤0.6

Cement paste fluidity, mm

230

210

200

Water reducing rate, %

15-27

15-25

14-22

Steel-bar corrosion

None

None

None


Addition Rates 
Sodium Naphthalene Sulphonate Formaldehyde can be added directly or added in after melt. It can be added during mixing and after-mixing. The afterward approach can achieve better result. The suggested addition rate is 0.75%. 
Sodium Naphthalene Sulphonate Formaldehyde Direction 
Prepare solutions as required. 
Direct use of powdery agent is allowed. Alternatively the addition of the agent is followed by water moisturization (water-cement ratio: 60%). 
The agent can be combined with other externally applied agents if pilot development or laboratory experiment succeeds. 

Sodium Naphthalene Sulfonate Formaldehyde Made in China

Notices:

1.Before use, mix ratio test must be done,especially for the first time using this product, to find out the correct mix rate and dosage.

2.High grading cement and reasonable sand/stone grading must be used to make high-strength or super high-strength concrete.

3.Water dosage must be strictly controlled to keep mixture unchanged.

4.The mix time should be prolonged for one minute;care should be taken to strengthen wet curing.

5.If used with liquid form , moisture should be deducted from concrete mixture.



Sodium Naphthalene Sulphonate Formaldehyde Package, Storage & Handling 
For powder: Woven fabric bag with plastic liner. Net weight: 25kg +/- 0.1 kg. 