Gibbsite Bauxite,Calcined Bauxite 88 From CNBM !!!

Inquire Now

OKorder Service Pledge

Quality Product, Order Online Tracking, Timely Delivery

OKorder Financial Service

Credit Rating, Credit Services, Credit Purchasing

Packaging Details:	In 25KG bags;1MT/1.25MT/1.35MT bags or as your requirements.
Delivery Detail:	15-30 days after contract

Product Description

Items	Al2O3	Fe2O3	B.D.	K2O+Na2O	CaO+Mgo	TiO2
88	88%min	1.5%max	3.25min	0.25%max	0.4%max	3.8%max
87	87%min	1.6%max	3.20min	0.25%max	0.4%max	3.8%max
86	86%min	1.8%max	3.15min	0.3%max	0.5%max	4%max
85	85%min	2.0%max	3.10min	0.3%max	0.5%max	4%max
83	83%min	2.0%max	3.05min	0.3%max	0.5%max	4%max
80	80%min	2.0%max	3.0min	0.3%max	0.5%max	4%max
78	75-78%	2.0%max	2.8-2.9	0.3%max	0.5%max	4%max

Size: 0-1mm,1-3mm,3-5mm,5-8mm,8-10mm,200mesh,325mesh or as your request.

Application

mainly used in aluminium metallurgy,aiso used in abrasive ,cement ,chemical, refractory

Gibbsite Bauxite,Calcined Bauxite 88 From CNBM !!!

Q: Coke is how to produce, what is its purpose?: Natural coke. Coke can be obtained by high-temperature carbonization of coal:

Q: What are the indicators of first grade coke and the two grade coke?: No greater than 12 is not greater than 0.6 not less than 80 not greater than 8 not greater than 1.9

Q: What is the phosphorus content in coke: Generally, the phosphorus content of coke is low, about 0.02%.The bituminous coal is heated to 950-1050 DEG C under the condition of air isolation

Q: Listen to a lot of people say that steel is now coke is not true?: But at present, the iron making technology without coke has not yet been relatively mature, and it is not dominant compared with the traditional ironmaking technology. Coke industry still has development prospects.

Q: The sulfur content of coal and coke in general, the coking process of sulfur content of coal into the output of sulfur content of coke compared to those who are high and low?: Of course, the sulfur content of coke is low. Coke quality requirements: two grade coke containing sulfur below 0.7%

Q: The chemical composition of coke m10.m25 refers to?: 1, coal washing ((M25 drum index) metallurgical coke crushing strength is (M10 drum index) metallurgical coke wear strength is reflected

Q: In the coke analysis index, M40% and M25% respectively mean what?: (2) mainly used in: Coal Science and Technology (first level), coal processing and utilization (level two), coal chemistry and coal quality analysis (level three)

Q: Effect of coke powder ratio on the index: 6, the size of coke in the blast furnace, coke screening is very important. We used the coke size requirements: large oven coke particle size greater than 40mm (1300--2000 square meters); small blast furnace coke particle size greater than 25 mm. But experiments show that some steel mills, coke size 40--25 mm good. More than 80mm of coke are screened to little change in the size range. This fragmentation of the coke uniform gap, small resistance furnace is running well.Purpose: various specifications of Shanxi foundry coke, metallurgical coke, coke car or high sulfur transport cars online sales. The specific indicators are as follows:Fixed carbon 83 or above; sulfur less than 0.5; 1.5 or less volatile; ash about E:Focal mechanism:Violin coke size 8 cm -150 cm:Metabituminous:Bulk modified coke:Size of 25 cm:

Q: What's the difference between coke and coke?: Higher than 550 DEG C, semi coke continues to decompose, precipitation of the remaining volatiles (the main component is hydrogen), semi coke weight loss at the same time contraction, the formation of cracks; temperature above the temperature of 800 degrees, the volume of semi coke hardens to form porous coke!

Q: How much coke is needed for a ton of iron: 1 tons of iron: iron ore + + coke 340kg + pulverized coal injection 130kg,The process of extracting iron from iron containing minerals, mainly iron oxides, is mainly composed of blast furnace, direct reduction, smelting reduction and plasma method. From the perspective of ironmaking is metallurgy, iron rust, inverse behavior gradually mineralized, simple, pure iron reduction from iron compounds. Pure iron is not common in actual production. More iron carbon alloy.

Send your message to us

*Email

*TEL

*Quantity

*Unit