The silica bricks for HBS
Silica fire brick for coke oven
High density silica fire brick
Semi-silics fire brick for coke oven

1.Silica brick manufature.
2.High refractoriness under load.
3.High heat conductivity.
4.Good thermal shock resistance.

Tech Data

Silica brick for glass furnace
Item:		GF-96A	GF-96B	GF-95A	GF-95B
SiO 2		≥96	≥96	≥95	≥95
Fe 2 O 3		≤0.8	≤1.0	≤1.2	≤1.2
Apparent porosity %		≤22(24)
Cold Crushing Strength MPa	Brick below20KG	≥35(30)
	Brick ≥20KG	≥30(25)
Refractoriness under load ºC		≥1680	≥1670	≥1660	≥1650
True density g/cm ³		≤2.34	≤2.34	≤2.35	≤2.35

Silica brick for coke oven
Item:	CO-94A	CO-94B
SiO2: %	≥94	≥94
Al 2 O 3 : %	≤ 1.5	≤ 1.5
Fe2O3: %	≤ 1.5	≤ 1.5
Refractoriness under load 0.2Mpa	≥ 1650ºC	≥ 1650ºC
Apparent porosity: %	≤ 22	≤ 24
Bulk density: g/cm ³	≤ 2.34	≤ 2.35
Cold crushing strength: MPa	≥30	≥25
Permanent linear change % (1450ºC ×2h)	0~0.2	0~0.2
Thermal expansion(1000ºC)	≤1.28	≤1.30

Silica brick for hot blast furnace
Item	HBF-95
SiO2	≥ 95
Al2O3	≤ 1.0
Fe2O3	≤1.3
Apparent porosity %	≤22(24)
Cold crushing strength MPa	≥45(35)
Remaining quarts %	≤1.0
Refractoriness under load ºC	≥1650
Creep(0.2Mpa ×1550ºC×50h) %	≤0.8
Thermal expansion coefficient (1000ºC) %	≤1.25
Apparent density g/cm ³	≤2.32

Q:Can iron oxide be used as refractory material?: Is widely used in this area. Mentioned refractory material of high school textbooks generally refers to three two aluminum oxide (alumina), alumina is also used as a refractory material, refractory crucible, porcelain, artificial gemstones.

Q:How much is the highest melting point of silicon?: Acidic silica brick refractories, softening temperature is as high as 1640 to 1670 DEG C, in the long-term use volume is relatively stable under high temperature. More than 94% silica content.

Q:Why is the highest brick coke oven temperature measuring point temperature not exceeding 1450: Brick belongs to refractory materials, with strong resistance to acid slag or acid solution erosion ability, high load softening temperature are excellent properties of silica brick, usually 1640-1680 C.

Q:Brick: An acid refractory consisting mainly of quartz and square quartz and a small amount of residual quartz and glass.More than 94% silica content. True density 2.35g/cm3. With acid resistance, slag erosion performance. Higher high temperature strength. The softening start temperature is 1620~1670 degrees. Long term use at high temperature without deformation. The thermal shock resistance is low (the heat exchange in water is 1~4 times). The natural silica is used as the raw material, and a proper amount of mineralizer is used to promote the transformation of quartz into quartz in the body. Slowly sintered at 1350~1430 DEG C in the reducing atmosphere. When heating up to 1450 degrees, the total volume of 1.5~2.2% expands, and the residual expansion can close the kerf and ensure the airtight and structural strength of the masonry.

Q:The brick is mainly used in the place?: Also used for high temperature bearing part of hot blast stove and acid open hearth furnace.

Q:The difference between clay refractory bricks and refractory brick in the application.: Brick bearing soft temperature and close to the melting point, high temperature strength, can be in high temperature (above 1400 degrees) under the condition of long-term use,

Q:The high thermal conductivity of silica brick and traditional brick what is the difference?: Brick, high thermal conductivity has been greatly improved in terms of morphology, crystal structure, physicochemical index. The structure and morphology of high thermal conductivity of silica brick,Structure and morphology of high thermal conductivity and the traditional brick brick magnified 20 times were compared, high thermal conductivity silica pore size distribution is more uniform and finer.

Q:The formula in the refractory brick, and firing curve, who knows?: Add 1.8-2.2% of the total weight of the main raw material, and then add lime milk, rolling for 10-15 minutes, and finally add pulp, rolling for 10-15 minutes, out of the mill, forming billet.

Q:What is acid refractory?: Refractory materials are mainly quartz glass products, combined with fused quartz products, silica brick and unshaped refractories. Semi siliceous refractory materials are generally attributed to this category. As for fireclay refractories, they are also classified as semi acidic or weakly acidic refractories. Also, zircon refractory and silicon carbide refractory for special acidic refractory materials are also classified into this category.

Q:Can not use it two brick: Acidic silica brick refractory material, has good ability in acid slag erosion

3. Manufacturer Capability
a)Trade Capacity
Nearest Port
Export Percentage
No.of Employees in Trade Department
Language Spoken:
b)Factory Information
Factory Size:
No. of Production Lines
Contract Manufacturing
Product Price Range